Search for: All records

Bimetallic nanomaterials have shown great potential across various fields of application. However, the synthesis of many bimetallic particles can be challenging due to the immiscibility of their constituent metals. In this study, we present a synthetic strategy to produce compositionally tunable silver–copper (Ag-Cu) bimetallic nanoparticles using plasma-driven liquid surface chemistry. By using a low-pressure nonthermal radiofrequency (RF) plasma that interacts with an Ag-Cu precursor solution at varying electrode distances, we identified that the reduction of Ag and Cu salts is governed by two “orthogonal” parameters. The reduction of Cu2+ is primarily influenced by plasma electrons, whereas UV photons play a key role in the reduction of Ag+. Consequently, by adjusting the electrode distance and the precursor ratios in the plasma–liquid system, we could control the composition of Ag-Cu bimetallic nanoparticles over a wide range. 

Gamma alumina (γ-Al2O3) is widely used as a catalyst and catalytic support due to its high specific surface area and porosity. However, synthesis of γ-Al2O3 nanocrystals is often a complicated process requiring high temperatures or additional post-synthetic steps. Here, we report a single-step synthesis of size-controlled and monodisperse, facetted γ-Al2O3 nanocrystals in an inductively coupled nonthermal plasma reactor using trimethylaluminum and oxygen as precursors. Under optimized conditions, we observed phase-pure, cuboctahedral γ-Al2O3 nanocrystals with defined surface facets. Nuclear magnetic resonance studies revealed that nanocrystal surfaces are populated with AlO6, AlO5 and AlO4 units with clusters of hydroxyl groups. Nanocrystal size tuning was achieved by varying the total reactor pressure yielding particles as small as 3.5 nm, below the predicted thermodynamic stability limit for γ-Al2O3. 

Abstract Silver nanoparticles (NPs) are extensively used in electronic components, chemical sensors, and disinfection applications, in which many of their properties depend on particle size. However, control over silver NP size and morphology still remains a challenge for many synthesis techniques. In this work, we demonstrate the surfactant-free synthesis of silver NPs using a low-pressure inductively coupled nonthermal argon plasma. Continuously forming droplets of silver nitrate (AgNO 3 ) precursor dissolved in glycerol are exposed to the plasma, with the droplet residence time being determined by the precursor flow rate. Glycerol has rarely been studied in plasma-liquid interactions but shows favorable properties for controlled NP synthesis at low pressure. We show that the droplet residence time and plasma power have strong influence on NP properties, and that improved size control and particle monodispersity can be achieved by pulsed power operation. Silver NPs had mean diameters of 20 nm with geometric standard deviations of 1.6 under continuous wave operation, which decreased to 6 nm mean and 1.3 geometric standard deviation for pulsed power operation at 100 Hz and 20% duty cycle. We propose that solvated electrons from the plasma and vacuum ultraviolet (VUV) radiation induced electrons produced in glycerol are the main reducing agents of Ag + , the precursor for NPs, while no significant change of chemical composition of the glycerol solvent was detected.